Modification of HVOF and cold spray deposited coatings via electron beam technology
 Vacek, Petr ; Šiška, Filip (referee) ; Čížek, Jan (advisor)
The aim of this thesis was to modify microstructure and coating-substrate interface of CoNiCrAlY coatings deposited by HVOF and cold spray on Inconel 718 substrates. Electron beam remelting and annealing in a protective atmosphere were used to modify the coatings. Microstructure, chemical and phase composition were analyzed. The effect of beam current, transversal velocity and beam defocus on remelted depth was evaluated. As-sprayed microstructure and chemical composition of coatings were analyzed and compared with remelted samples. The effect of annealing of the as-sprayed and remelted samples was evaluated. Remelted layers exhibited dendritic structure. Chemical composition changed only after remelting of interface and part of a substrate. When only the coating was remelted, chemical composition remained the same. Phases coarsened after the annealing. Chemical composition changed after annealing due to the diffusion.
Detailed record
Modification of HVOF and cold spray deposited coatings via electron beam technology
 Vacek, Petr ; Šiška, Filip (referee) ; Čížek, Jan (advisor)
The aim of this thesis was to modify microstructure and coating-substrate interface of CoNiCrAlY coatings deposited by HVOF and cold spray on Inconel 718 substrates. Electron beam remelting and annealing in a protective atmosphere were used to modify the coatings. Microstructure, chemical and phase composition were analyzed. The effect of beam current, transversal velocity and beam defocus on remelted depth was evaluated. As-sprayed microstructure and chemical composition of coatings were analyzed and compared with remelted samples. The effect of annealing of the as-sprayed and remelted samples was evaluated. Remelted layers exhibited dendritic structure. Chemical composition changed only after remelting of interface and part of a substrate. When only the coating was remelted, chemical composition remained the same. Phases coarsened after the annealing. Chemical composition changed after annealing due to the diffusion.
Detailed record

Interested in being notified about new results for this query?
Subscribe to the RSS feed.
Digital Repository :: Search :: Submit :: Personalize :: Help
Powered by Invenio v1.1.2
Maintained by admin.invenio@techlib.cz
This site is also available in the following languages:
Česky  English